Bitumen Number 40

Bitumen Number 40 Description

Bitumen 40 is a type of hard grade building asphalt with penetration starting from #40 that is why it is famous asphalt number 40. Bitumen Number 40 is available in bag and drum also the bulk tanker. This grade of asphalt building material is mostly using in the eastern Asia market especially Taiwan and China also the Philippine and Indonesia. Bitumen grade 40 is the most consumable hard asphalt which is a semi-solid grade of pure petroleum bitumen categorized in polycyclic aromatic hydrocarbons is normally used for different purposes in the construction business.

Blown Asphalt No. 40 Applications

1. For underground moisture, waterproofing works
2. For nuclear power engineering, pipeline engineering, bottom anticorrosion, asphalt production of the production
3. For waterproofing membrane, moisture-proof paper production, etc.
4. For Anti-corrosion paint and waterproof production
5. Used for road and bridge caulking use

Blown Asphalt No. 40 Specs

Technical indicators	10
Penetration (25 ° C, 100 g, 5 s) / (0.1 mm)	10-26
The ductility (25 ° C, 5 cm / min) / cm is not less than	1.5
Softening point (ball method) / ℃ not less than	95
Solubility (trichloroethylene) /% is not less than	99.5
Evaporation loss (163 ° C, 5 h) /% no more than	1
After evaporation, the penetration ratio (25 ℃) /% is not less than	65
Flashpoint (open cup) / ℃ not less than	230
Brittle / ℃	report

Bitumen No.40 Packing

Bitumen Number 40 in various packing including kraft bag, meltable plastic bag, drum, and bulk, it is made by hot air in a controlled process until the desired specification is reached. Bitumen Number 40 can be supplied in volume quantity as well. Bitumen #40 means the softening point is 115°c and penetration is 15 desi millimeter is produced in compliance and conformity to ASTM standard and meets the mentioned specification.

Bitumen Number 30

Bitumen Number 30 Description

Bitumen30 is a type of hard grade building asphalt with penetration starting from #30 that is why it is famous asphaltum number 30. Bitumen Number 30 is available in bag and drum also the bulk tanker. This grade of asphalt building material is mostly using in the eastern Asia market especially Taiwan and China also the Philippine and Indonesia. Bitumen grade 30 is the most consumable hard asphalt which is a semi-solid grade of pure petroleum bitumen categorized in polycyclic aromatic hydrocarbons is normally used for different purposes in the construction business.

Blown Asphalt N0. 30 Applications

1. For underground moisture, waterproofing works
2. For nuclear power engineering, pipeline engineering, bottom anticorrosion, asphalt production of the production
3. For waterproofing membrane, moisture-proof paper production, etc.
4. For Anti-corrosion paint and waterproof production
5. Used for road and bridge caulking use

Blown Asphalt No. 30 Specs

Technical indicators	10
Penetration (25 ° C, 100 g, 5 s) / (0.1 mm)	10-26
The ductility (25 ° C, 5 cm / min) / cm is not less than	1.5
Softening point (ball method) / ℃ not less than	95
Solubility (trichloroethylene) /% is not less than	99.5
Evaporation loss (163 ° C, 5 h) /% no more than	1
After evaporation, the penetration ratio (25 ℃) /% is not less than	65
Flashpoint (open cup) / ℃ not less than	230
Brittle / ℃	report

Bitumen No.30 Packing

Bitumen Number 30 in various packing including kraft bag, meltable plastic bag, drum, and bulk, it is made by hot air in a controlled process until the desired specification is reached. bitumen Number 30 can be supplied in volume quantity as well. Bitumen #30 means the softening point is 115°c and penetration is 15 desi millimeter is produced in compliance and conformity to Astm standard and meets the mentioned specification.

Bitumen Number 10

Bitumen Number 10 Description

Bitumen 10 is a type of hard grade building asphalt with penetration starting from #10 that is why it is famous asphaltum number 10. Bitumen Number 10 is available in bag and drum also the bulk tanker. This grade of asphalt building material is mostly using in the eastern Asia market especially Taiwan and China also the Philippine and Indonesia. Bitumen grade 10 is the most consumable hard asphalt which is a semi-solid grade of pure petroleum bitumen categorized in polycyclic aromatic hydrocarbons is normally used for different purposes in the construction business.

Blown Asphalt N0. 10 Applications

1. For underground moisture, waterproofing works
2. For nuclear power engineering, pipeline engineering, bottom anticorrosion, asphalt production of the production
3. For waterproofing membrane, moisture-proof paper production, etc.
4. For Anti-corrosion paint and waterproof production
5. Used for road and bridge caulking use

Blown Asphalt No. 10 Specs

Technical indicators	10
Penetration (25 ° C, 100 g, 5 s) / (0.1 mm)	10-26
The ductility (25 ° C, 5 cm / min) / cm is not less than	1.5
Softening point (ball method) / ℃ not less than	95
Solubility (trichloroethylene) /% is not less than	99.5
Evaporation loss (163 ° C, 5 h) /% no more than	1
After evaporation, the penetration ratio (25 ℃) /% is not less than	65
Flashpoint (open cup) / ℃ not less than	230
Brittle / ℃	report

Bitumen No.10 Packing

Bitumen Number 10 in various packing including kraft bag, meltable plastic bag, drum, and bulk, it is made by hot air in a controlled process until the desired specification is reached. bitumen Number 10 can be supplied in volume quantity as well. Bitumen #10 means the softening point is 115°c and penetration is 15 desi millimeter is produced in compliance and conformity to Astm standard and meets the mentioned specification.

Oxidized Bitumen 75/25

Oxidized Bitumen 75/25 Description

Oxidized Bitumen 75/25 is an oxidized Bitumen produced by oxidizing a selected petroleum asphalts without adding the catalyst. Bitumen 75/25 has a high softening point, high flash point and it is highly stable during melting. This kind of Blown Asphalt is mostly using in the Mediterranean and especially the morocco market.

Blown Asphalt 75/25 is produced by the air-blowing of penetration grade bitumen. This is done at high temperatures, resulting in a material of a much higher penetration index.

Bitumen 75/25 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The designation of the Oxidised bitumen 75/25 refers to the midpoint of the softening point acceptance criteria.

Blown Asphalt is a solid or semi-black solid material and gradually liquid when heated. Oxidized Bitumen grades are blown or oxidized bitumen‘s which are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumens and a variety of uses in industrial applications.

Bitumen 75/25 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Bitumen 75/25 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 75/25 Applications

Blown Asphalt 75/25 grades are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumen and enables the product to serve a variety of uses in industrial applications. These grades are suitable for sealing saw cuts and joints where there is expected to be the minimum amount of moving in the joint. Their wide temperature range prevents bleeding in high-temperature applications. They can also be used for industrial applications such as pipe coating, roofing, waterproofing, flooring, mastics, sound damping, carpet backing, adhesive and electrical applications. Hard bitumen under controlled temperature conditions is widely used as an anti-slip layer compound in the piling industry, for the manufacture of roofing felts, the roofing and waterproofing industries, for sound dampening felts and undercarriage sealant in the automotive industry, electric cable joint protection, joint filling compound, sealant compound, and many others. Also used in sealing saw cuts and joints where expected movements are minimum.

Technical Advantages of Blown Asphalt 75/25

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Bitumen material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Blown Asphalt 75/25  to avoid overheating

Oxidized Bitumen 75/25  is a dark industrial bitumen. Petroleum residue modified by the oxidation process. In addition, Blown Asphalt is produced by passing air through bitumen under a controlled temperature state. Its stability ranges from highly viscous to solid. Blown Asphalt grade has technical advantages such as durability, flexibility, water-resistant and chemical stability. There is also a different grade of blown bitumen.
Blown Grade Asphalt shall be broken up into small pieces and heated slowly to the application temperature of 220ºC to 230ºC.

Packing of Oxidized Bitumen 75/25

Oxidized Bitumen 75/25  in various packing, including bitumen 75/25 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box, and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Technical Data Sheet of Blown Asphalt 75/25

Bitumen 75/25	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	30/40
Softening point °c	ASTM  D36	°C	70/80
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.T.O 102	—	Negative

Oxidized Bitumen 75/35

Oxidized Bitumen 75/35 Description

Blown Asphalt 75/35 is an oxidized Bitumen produced by oxidizing a selected petroleum asphalts without adding the catalyst. Bitumen 75/35 has a high softening point, high flash point and it is highly stable during melting. This kind of Blown Asphalt is mostly using in the Mediterranean and especially the morocco market.

Blown Asphalt 75/35 is produced by the air-blowing of penetration grade bitumen. This is done at high temperatures, resulting in a material of a much higher penetration index.

Bitumen 75/35 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The designation of the Oxidised bitumen 75/35 refers to the midpoint of the softening point acceptance criteria.

Blown Asphalt is a solid or semi-black solid material and gradually liquid when heated. Oxidized Bitumen grades are blown or oxidized bitumen‘s which are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumens and a variety of uses in industrial applications.

Bitumen 75/35 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Bitumen 75/35 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 75/35 Applications

Blown Asphalt 75/35 grades are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumen and enables the product to serve a variety of uses in industrial applications. These grades are suitable for sealing saw cuts and joints where there is expected to be the minimum amount of moving in the joint. Their wide temperature range prevents bleeding in high-temperature applications. They can also be used for industrial applications such as pipe coating, roofing, waterproofing, flooring, mastics, sound damping, carpet backing, adhesive and electrical applications. Hard bitumen under controlled temperature conditions is widely used as an anti-slip layer compound in the piling industry, for the manufacture of roofing felts, the roofing and waterproofing industries, for sound dampening felts and undercarriage sealant in the automotive industry, electric cable joint protection, joint filling compound, sealant compound, and many others. Also used in sealing saw cuts and joints where expected movements are minimum.

Technical Advantages of Blown Asphalt 75/35

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Bitumen material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Blown Asphalt 75/35  to avoid overheating

Oxidized Bitumen 75/35  is a dark industrial bitumen. Petroleum residue modified by the oxidation process. In addition, Blown Asphalt is produced by passing air through bitumen under a controlled temperature state. Its stability ranges from highly viscous to solid. Blown Asphalt grade has technical advantages such as durability, flexibility, water-resistant and chemical stability. There is also a different grade of blown bitumen.
Blown Grade Asphalt shall be broken up into small pieces and heated slowly to the application temperature of 220ºC to 230ºC.

Packing of Oxidized Bitumen 75/35

Blown Asphalt 75/35  in various packing, including bitumen 75/35 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box, and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Technical Data Sheet of Blown Asphalt 75/35

Bitumen 75/35	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	30/40
Softening point °c	ASTM  D36	°C	70/80
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.T.O 102	—	Negative

Oxidized Bitumen 90/10

Oxidized Bitumen 90/10 Description

Oxidized Bitumen 90/10 (in other words, oxidized Asphalt 90/10, blown bitumen 90/10) is Semi Solid grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business. Oxidized asphalt 90/10 is based on petroleum bitumen which is made by oxidized asphalt 60/70 by hot air. The numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 90/10 Applications

Oxidized bitumen 90/10 uses in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, crack seal and repairmen, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The Oxidized asphalt 90/10 products are for paving. also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, a base for synthetic turf; typical uses for Blown Asphalt 90/10 90/10 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. Oxidized bitumen 90/10 is using the insulation and isolation bitumen membrane sheet. Also, Car undercoating Automobile industry is especially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof, and noise proof for automobile undercoating.

The Blown Asphalt 90/10 90/10 should be heated double temperature against the softening point to be able to have flow and viscosity. To use Blown Asphalt 90/10 90/10, surfaces must be dry, clean, and free of loose particles, formwork, curing products, irregularities, slurry, etc.

Storage/handling of Blown Asphalt 90/10

Bitumen 90/10 has 10 years of validity with multi-time heating and cooling, please refer to MSDS.

Packing of Blown Asphalt 90/10

Various pickings are available for customer’s purpose and conveniences. bitumen 90/10 in various packing including Kraft bag, meltable plastic bag, drum, and bulk Blown Asphalt 90/10 90/10 from penetration grade bitumen, which is blown by hot air in a controlled process until the desired specification is reached. Blown Asphalt 90/10 can be supplied in any grade and are designated by two numbers to indicate the softening point and penetration ranges. The bitumen grade 90/10 means the softening point is 90°c and penetration is 10 desi millimeter is produced in compliance and conformity with ASTM standard and meets the following specification.

Specification of Oxidized Bitumen 90/10

Analysis of bitumen 90/10

Bitumen 90/10	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	5/15
Softening point °c	ASTM  D36	°C	85/95
Ductility @25 °c	ASTM  D113	Cm	1.5min
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Oxidized Bitumen 90/15

Oxidized Bitumen 90/15

At the Oxidized bitumen 90/15 production reactor, during the air acting, the mixture of the two Vacuum Bottom (VB) and Vacuum Silas (VS) feedstock is put under a special degree of pressure and temperature between 200-300˚C of which the hydrogen atoms content in bitumen molecular oxidize to the oxygen of the air, and obtains with higher hydrocarbons polymerization reaction that has lower penetration and higher softening points than the primary pure bitumen. This kind of bitumen 90/15 has the softening point of 90 and permeability of 15.
Oxidized bitumen is a specially formulated plastic for construction. Oxidized bitumen characterized by being a product of great thermal amplitude. Oxidized bitumen has the flexibility to cold, has no sag at high temperatures, and has good adhesion. It can be applied to any kind of work. Oxidized bitumen is available in different grades. Bitumen 90/15 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Bitumen 90/15 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 90/15 Applications

Oxidized bitumen 90/15 uses in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, crack seal and repairmen, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The Oxidized asphalt 90/15 products are for paving. also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, a base for synthetic turf; typical uses for oxidized bitumen 90/15 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. Oxidized bitumen 90/15 is using the insulation and isolation bitumen membrane sheet. Also, Car undercoating Automobile industry is especially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof, and noise proof for automobile undercoating.

Oxidized bitumen 90/15 should be heated double temperature against the softening point to be able to have flow and viscosity. To use oxidized bitumen 90/15, surfaces must be dry, clean, and free of loose particles, formwork, curing products, irregularities, slurry, etc.

• Oxidized bitumen is used as a sealing of expansion joints.
• Oxidized bitumen is used as a repair of joints or cracks.
• Oxidized bitumen is used as a fixation of parquet floors.
• Oxidized bitumen is used as an adhesive to be used in thermal insulation.
• Oxidized bitumen is used as a repair of unexposed cracks.
• Oxidized bitumen is used as bonding of wet briquettes
• Oxidized bitumen is used in various industries like roofing, isolation, insulation flooring, mastics, pipe coatings, electrical applications.

Technical Advantages of Oxidized Asphalt 90/15

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Asphalt material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Oxidized Asphalt 90/15 to avoid overheating.

Packing of Oxidized Asphalt 90/15

Oxidized Asphalt 90/15 in various packing, including bitumen 90/15 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box, and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Oxidized Asphalt 90/15 Specifications

Bitumen 90/15	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	10/20
Softening point °c	ASTM  D36	°C	85/95
Ductility @25 °c	ASTM  D113	Cm	1.5min
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Oxidized Bitumen 90/40

Oxidized Bitumen 90/40 Description

Oxidized bitumen 90/40 (in other words, Blown asphalt 90/40, blown bitumen 90/40) is Semi Solid grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business. blown asphalt 90/40 is based on petroleum bitumen which is made by blowing asphalt 60/70 by very hot air. The numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM D5.
Oxidized Asphalt is a solid or semi-black solid material and gradually liquid when heated, oxidized asphalt is the predominant content bitumen, asphalt, molten (oils), and aromatic resins. The oxidized asphalt or blown asphalt is producing in different softening point and penetration.

Oxidized Bitumen 90/40 Applications

Blown Asphalt 90/40 is a semi-solid oxidized grade of pure petroleum bitumen categorized in polycyclic aromatic hydrocarbons that are normally used for different purposes in the construction business.

Blown Asphalt 90/40 is widely used as an anti-slip layer compound in the piling industry, for the manufacture of roofing felts, the roofing and waterproofing industries, for sound dampening felts and undercarriage sealant in the automotive industry, electric cable joint protection, joint filling compound, carpet-backing, corrosion protection, acoustic panels, chemical, fuel, Manufacture of paints, sealant compound, and many others. Also used in sealing saw cuts and joints where expected movements are minimum. It is also used in the manufacturing of bituminous marine mastic for the oil & gas pipeline joints. Further, Blown Asphalt is used in the manufacture of bituminous marine mastic, which is required for the oil and gas pipeline joints.

Blown Asphalt has several usages in the industry

Oil and Gas industries:

• Coating materials for pipelines and pipe joints of Oil Also Gas Pipelines.

Electrical industries:

• The sealant of wire coating

Waterproofing industries:

• Building roofing felts in factories and first materials components who are producing waterproofing roofing felt sheets

Bitumen and Asphalt:

• Road paving, Asphalt, construction.
• Making Sound insulation layers.
• Car tires and lining.

Technical Advantages of Oxidized Bitumen 90/40

• Durability
• Flexibility
• Water Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Bitumen material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the RAHA modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Blown Asphalt 90/40 to avoid overheating.

Packing of Oxidized Bitumen 90/40

Blown Asphalt 90/40 in various packing, including bitumen 90/40 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box, and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Technical Data Sheet of Blown Asphalt 90/40

Bitumen 90/40	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	35/45
Softening point °c	ASTM  D36	°C	85/95
Ductility @25 °c	ASTM  D113	Cm	5.5min
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Oxidized Bitumen 105/35

Oxidized Bitumen 105/35 Description

Oxidized bitumen 105/35 is a good grade of oxidized asphalt to use as bonding compounds as hot melt adhesive at an application rate of approximately 1 Kg/m3 to bond the preformed sheets together and to structure which is made by Oxidized bitumen 60/70 by hot air. Blown bitumen 105/35 is a semi-solid oxidized grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business.

Oxidized Bitumen 105/35 Applications

Oxidized bitumen 105/35 uses in the chemical, fuel, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, paint, crack seal and repairmen, civil works, roofing, construction business; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The bitumen 105/35 products are for paving. also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, the base for synthetic turf; typical uses for bitumen 105/35 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing. Blown bitumen 105/35 is using the insulation and isolation bitumen membrane sheet. The car undercoating Automobile industry is especially required for blown bitumen. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof, and noise proof for automobile undercoating.
Blown Asphalt 105/35 should be heated double temperature against the softening point to be able to have flow and viscosity. To use blown bitumen 105/35, surfaces must be dry, clean, and free of loose particles, formwork, curing products, irregularities, slurry, etc.

Storage/handling of blown bitumen 105/35

bitumen 105/35 has 10 years validity with multi-time heating and cooling, please refer to MSDS.

Packing of blown bitumen 105/35

Different packing is available for the customer’s purpose and convenience. bitumen 105/35 in different packing including Kraft bag, meltable plastic bag, drum, and bulk. Blown asphalt 105/35 from penetration grade bitumen, which is blown by hot air in a controlled process until the desired specification is reached. bitumen 105/35 can be supplied in any grade and are designated by two numbers to show the softening point and penetration ranges. The bitumen grade 105/35 means the softening point is 105 and penetration is 35 desi millimeters is produced in compliance and conformity with ASTM standard and meets the following specification.

Specification of blown bitumen 105/35

Analysis bitumen 105/35

Bitumen 105/35	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	30/40
Softening point °c	ASTM  D36	°C	100/110
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.

Oxidized Bitumen 105/15

Oxidized Bitumen 105/15 Description

Oxidized asphalt 105/15 (another word, blown asphalt 105/15, oxidized bitumen 105/15) is Semi Solid grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business. Oxidized asphalt 105/15 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 105/15 Applications

Oxidized asphalt 105/15 uses in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, crack seal and repairmen, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The oxidized asphalt 105/15 products are for paving. also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, a base for synthetic turf; typical uses for asphalt 105/15 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. Asphalt 105/15 is using the insulation and isolation bitumen membrane sheet. The car undercoating Automobile industry is especially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof, and noise proof for automobile undercoating. The oxidized asphalt 105/15 should be heated double temperature against the softening point to support have flow and viscosity. To use asphalt 105/15, surfaces must be dry, clean and after loose particles, formwork, curing products, irregularities, slurry, etc.

Technical Advantages of Blown Bitumen 105/15

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Storage and Handling

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

The note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Blown Bitumen material should be broken up before placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Blown Bitumen 105/15 to avoid overheating.

Blown Asphalt 105/15 CHARACTERISTICS

CHARACTERISTIC	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	10/20
Softening point °c	ASTM D36	°C	100/110
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Blown asphalt 105/15 Packing

Various packings are available for customer’s purpose and conveniences. TAVOIL CO is the manufacturer of asphalt 105/15 in various packing including Kraft bag, meltable plastic bag, drum, and bulk oxidized asphalt 105/15 from penetration grade bitumen.

TAVOIL asphalt 105/15 perchance is supplied in any grade and is designated by two numbers to indicate the softening point and penetration ranges. The oxidized asphalt grade 105/15 means the softening point is 105 and penetration are 15 desi millimeters is produced in compliance and conformity with ASTM standard and meets the following specification.