Oxidized Bitumen 75/25

Oxidized Bitumen 75/25 Description

Oxidized Bitumen 75/25 is an oxidized Bitumen produced by oxidizing a selected petroleum asphalts without adding the catalyst. Bitumen 75/25 has a high softening point, high flash point and it is highly stable during melting. This kind of Blown Asphalt is mostly using in the Mediterranean and especially the morocco market.

Blown Asphalt 75/25 is produced by the air-blowing of penetration grade bitumen. This is done at high temperatures, resulting in a material of a much higher penetration index.

Bitumen 75/25 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The designation of the Oxidised bitumen 75/25 refers to the midpoint of the softening point acceptance criteria.

Blown Asphalt is a solid or semi-black solid material and gradually liquid when heated. Oxidized Bitumen grades are blown or oxidized bitumen‘s which are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumens and a variety of uses in industrial applications.

Bitumen 75/25 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Bitumen 75/25 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 75/25 Applications

Blown Asphalt 75/25 grades are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumen and enables the product to serve a variety of uses in industrial applications. These grades are suitable for sealing saw cuts and joints where there is expected to be the minimum amount of moving in the joint. Their wide temperature range prevents bleeding in high-temperature applications. They can also be used for industrial applications such as pipe coating, roofing, waterproofing, flooring, mastics, sound damping, carpet backing, adhesive and electrical applications. Hard bitumen under controlled temperature conditions is widely used as an anti-slip layer compound in the piling industry, for the manufacture of roofing felts, the roofing and waterproofing industries, for sound dampening felts and undercarriage sealant in the automotive industry, electric cable joint protection, joint filling compound, sealant compound, and many others. Also used in sealing saw cuts and joints where expected movements are minimum.

Technical Advantages of Blown Asphalt 75/25

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Bitumen material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Blown Asphalt 75/25  to avoid overheating

Oxidized Bitumen 75/25  is a dark industrial bitumen. Petroleum residue modified by the oxidation process. In addition, Blown Asphalt is produced by passing air through bitumen under a controlled temperature state. Its stability ranges from highly viscous to solid. Blown Asphalt grade has technical advantages such as durability, flexibility, water-resistant and chemical stability. There is also a different grade of blown bitumen.
Blown Grade Asphalt shall be broken up into small pieces and heated slowly to the application temperature of 220ºC to 230ºC.

Packing of Oxidized Bitumen 75/25

Oxidized Bitumen 75/25  in various packing, including bitumen 75/25 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box, and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Technical Data Sheet of Blown Asphalt 75/25

Bitumen 75/25	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	30/40
Softening point °c	ASTM  D36	°C	70/80
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.T.O 102	—	Negative

Oxidized Bitumen 75/35

Oxidized Bitumen 75/35 Description

Blown Asphalt 75/35 is an oxidized Bitumen produced by oxidizing a selected petroleum asphalts without adding the catalyst. Bitumen 75/35 has a high softening point, high flash point and it is highly stable during melting. This kind of Blown Asphalt is mostly using in the Mediterranean and especially the morocco market.

Blown Asphalt 75/35 is produced by the air-blowing of penetration grade bitumen. This is done at high temperatures, resulting in a material of a much higher penetration index.

Bitumen 75/35 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The designation of the Oxidised bitumen 75/35 refers to the midpoint of the softening point acceptance criteria.

Blown Asphalt is a solid or semi-black solid material and gradually liquid when heated. Oxidized Bitumen grades are blown or oxidized bitumen‘s which are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumens and a variety of uses in industrial applications.

Bitumen 75/35 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Bitumen 75/35 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 75/35 Applications

Blown Asphalt 75/35 grades are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumen and enables the product to serve a variety of uses in industrial applications. These grades are suitable for sealing saw cuts and joints where there is expected to be the minimum amount of moving in the joint. Their wide temperature range prevents bleeding in high-temperature applications. They can also be used for industrial applications such as pipe coating, roofing, waterproofing, flooring, mastics, sound damping, carpet backing, adhesive and electrical applications. Hard bitumen under controlled temperature conditions is widely used as an anti-slip layer compound in the piling industry, for the manufacture of roofing felts, the roofing and waterproofing industries, for sound dampening felts and undercarriage sealant in the automotive industry, electric cable joint protection, joint filling compound, sealant compound, and many others. Also used in sealing saw cuts and joints where expected movements are minimum.

Technical Advantages of Blown Asphalt 75/35

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Bitumen material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Blown Asphalt 75/35  to avoid overheating

Oxidized Bitumen 75/35  is a dark industrial bitumen. Petroleum residue modified by the oxidation process. In addition, Blown Asphalt is produced by passing air through bitumen under a controlled temperature state. Its stability ranges from highly viscous to solid. Blown Asphalt grade has technical advantages such as durability, flexibility, water-resistant and chemical stability. There is also a different grade of blown bitumen.
Blown Grade Asphalt shall be broken up into small pieces and heated slowly to the application temperature of 220ºC to 230ºC.

Packing of Oxidized Bitumen 75/35

Blown Asphalt 75/35  in various packing, including bitumen 75/35 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box, and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Technical Data Sheet of Blown Asphalt 75/35

Bitumen 75/35	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	30/40
Softening point °c	ASTM  D36	°C	70/80
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.T.O 102	—	Negative

Oxidized Bitumen 85/25

Oxidized Bitumen 85/25 Description

Oxidized Bitumen 85/25 or Oxidized Asphalt 85/25 is produced by blowing hot air into the penetration bitumen. This action makes the bitumen more rubbery than its original formula and it becomes harder bitumen. This bitumen recovery the weight loss under heating. Due to low thermal sensitivity, the softening point is much higher than regular bitumen and the penetration index (PI) is higher than road construction bitumen (8>PI>2) due to the letter has a gel-like structure because of asphalt accumulation.

Oxidized Bitumen 85/25 is produced by the air-blowing of penetration grade bitumen. This is done at high temperatures, resulting in a material of a much higher penetration index. Bitumen 85/25 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The designation of the Oxidized Bitumen 85/25 refers to the midpoint of the softening point acceptance criteria.

Bitumen 85/25 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Blown Asphalt 85-25 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 85/25 Applications

Oxidized Bitumen 85/25 is a solid or semi-black solid material and gradually liquid when heated. Oxidized Bitumen grades are blown or oxidized Asphalt‘s which are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumens and a variety of uses in industrial applications.

Oxidized Bitumen 85/25 is widely used as an anti-slip layer compound in the piling industry, for the manufacture of roofing felts, the roofing and waterproofing industries, for sound dampening felts and undercarriage sealant in the automotive industry, electric cable joint protection, joint filling compound,  carpet-backing, corrosion protection, acoustic panels, chemical, fuel, Manufacture of paints, sealant compound, and many others. Also used in sealing saw cuts and joints where expected movements are minimum. It is also used in the manufacturing of bituminous marine mastic for the oil & gas pipeline joints. Further, Oxidized Bitumen is used in the manufacture of bituminous marine mastic, which is required for the oil and gas pipeline joints.

• Oxidized bitumen is used as a sealing of expansion joints.
• Oxidized bitumen is used as a repair of joints or cracks.
• Oxidized bitumen is used as a fixation of parquet floors.
• Oxidized bitumen is used as an adhesive to be used in thermal insulation.
• Oxidized bitumen is used as a repair of unexposed cracks.
• Oxidized bitumen is used as bonding of wet briquettes
• Oxidized bitumen is used in various industries like roofing, isolation, insulation flooring, mastics, pipe coatings, electrical applications.

Technical Advantages of Oxidized Bitumen 85/25

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Bitumen material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

Bitumen 85/25 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

The Oxidized Bitumen 85/25 should be heated double temperature against the softening point to be able to have flow and viscosity.

Surfaces must be dry, clean, and free of loose particles, formwork, curing products, irregularities, slurry, etc.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Oxidized Bitumen 85/25 to avoid overheating. For Health and Safety information, please make reference to the relevant MSDS.

Packing of Blown Asphalt 85/25

Oxidized Bitumen 85/25 in various packing, including bitumen 85/25 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box, and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Technical Data Sheet of Blown Asphalt 85/25

Bitumen 85/25	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	20/30
Softening point °c	ASTM  D36	°C	80/90
Ductility @25 °c	ASTM  D113	Cm	3 min
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T 102	—	Negative

Oxidized Bitumen 85/35

Oxidized Bitumen 85/35 Description

Oxidized Bitumen 85/35 or Oxidized Bitumen is produced by blowing hot air into the penetration bitumen. This action makes the bitumen more rubbery than its original formula and it becomes harder bitumen. This bitumen recovery the weight loss under heating. Due to low thermal sensitivity, the softening point is much higher than regular bitumen and the penetration index (PI) is higher than road construction bitumen (8>PI>2) due to the letter has a gel-like structure because of asphalt accumulation.

Oxidized Bitumen 85/35 is produced by the air-blowing of penetration grade bitumen. This is done at high temperatures, resulting in a material of a much higher penetration index. Bitumen 85/35 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The designation of the Blown Asphalt 85/35 refers to the midpoint of the softening point acceptance criteria.

Bitumen 85/35 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Oxidized Bitumen 85-35 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 85/35 Applications

Oxidized Bitumen 85/35 is a solid or semi-black solid material and gradually liquid when heated. Oxidized Bitumen grades are blown or oxidized Asphalt‘s which are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumens and a variety of uses in industrial applications.

This bitumen is mostly used in industry, such as roof insulation, flooring, industrial mastic, pipe coating, and paints. Specification of Blown Asphalt is categorized based on softening points and penetration rates. Also, Blown Asphalt 85/35 using as raw material for bitumen coat, roofing, insulation, and isolation bitumen membrane sheet.

Technical Advantages of Blown Asphalt 85/35

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Blown Asphalt material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the RAHA modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the blown asphalt then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Blown Asphalt 85/35 to avoid overheating. For Health and Safety information, please make reference to the relevant MSDS.

The Blown Asphalt 85/35 should be heated double temperature against the softening point to be able to have flow and viscosity.

Packing of Oxidized Bitumen 85/35

RAHA GROUP is the manufacturer of Blown Asphalt 85/35 in various packing, including bitumen 85/35 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallet can load to the 20ft container.

Technical Data Sheet of Blown Asphalt 85/35

Bitumen 85/35	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	30/40
Softening point °c	ASTM  D36	°C	80/90
Ductility @25 °c	ASTM  D113	Cm	1.5min
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flash point °c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.T.O 102	—	Negative

Oxidized Bitumen 85/40

Oxidized Bitumen 85/40 Description

Oxidized Bitumen 85/40 or Blown bitumen is produced by blowing hot air into the penetration bitumen. This action makes the bitumen more rubbery than its original formula and it becomes harder bitumen. This bitumen recovery the weight loss under heating. Due to low thermal sensitivity, the softening point is much higher than regular bitumen and the penetration index (PI) is higher than road construction bitumen (8>PI>2) due to the letter has a gel-like structure because of asphalt accumulation. Oxidized bitumen 85/40 is a special and most usable grade in Scandinavia.

Oxidized Bitumen 85/40 is produced by the air-blowing of penetration grade bitumen. This is done at high temperatures, resulting in a material of a much higher penetration index. Bitumen 85/40 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The designation of the Oxidized Bitumen 85/40 refers to the midpoint of the softening point acceptance criteria.

Bitumen 85/40 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Bitumen 85/40 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 85/40 Applications

Oxidized Bitumen 85/40 is a solid or semi-black solid material and gradually liquid when heated. Oxidized Bitumen grades are blown or oxidized Asphalt‘s which are produced by passing air through soft bitumen under controlled temperature conditions. This process gives the bitumen more rubbery properties than penetration or hard grade bitumens and a variety of uses in industrial applications.

This bitumen is mostly used in industry, such as roof insulation, flooring, industrial mastic, pipe coating, and paints. Specification of Oxidized bitumen is categorized based on softening points and penetration rates. Also, Oxidised bitumen 85/40 using as raw material for bitumen coat, roofing, insulation, and isolation bitumen membrane sheet.

Technical Advantages of Oxidized Bitumen 85/40

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Bitumen material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Oxidized Bitumen 85/40 to avoid overheating. For Health and Safety information, please make reference to the relevant MSDS.

Application of Oxidized Bitumen 85/40

Oxidized Bitumen 85/40 is a dark industrial bitumen. Petroleum residue modified by the oxidation process. In addition, Oxidized Bitumen is produced by passing air through bitumen under a controlled temperature state. Its stability ranges from highly viscous to solid. Oxidized Bitumen grade has technical advantages such as durability, flexibility, water-resistant and chemical stability. There is also a different grade of oxidized bitumen.

The Oxidised Bitumen 85/40 should be heated double temperature against the softening point to be able to have flow and viscosity.

Packing of Oxidized Bitumen 85/40

Oxidized Bitumen 85/40 in various packing, including bitumen 85/40 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Technical Data Sheet of Oxidized Bitumen 85/40

Bitumen 85/40	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	35/40
Softening point °c	ASTM D36	°C	80/90
Ductility @25 °c	ASTM D113	Cm	3
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	260 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99 min
Spot test	A.A.S.H.O.T 102	—	Negative

Oxidized Bitumen 90/10

Oxidized Bitumen 90/10 Description

Oxidized Bitumen 90/10 (in other words, oxidized Asphalt 90/10, blown bitumen 90/10) is Semi Solid grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business. Oxidized asphalt 90/10 is based on petroleum bitumen which is made by oxidized asphalt 60/70 by hot air. The numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 90/10 Applications

Oxidized bitumen 90/10 uses in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, crack seal and repairmen, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The Oxidized asphalt 90/10 products are for paving. also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, a base for synthetic turf; typical uses for Blown Asphalt 90/10 90/10 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. Oxidized bitumen 90/10 is using the insulation and isolation bitumen membrane sheet. Also, Car undercoating Automobile industry is especially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof, and noise proof for automobile undercoating.

The Blown Asphalt 90/10 90/10 should be heated double temperature against the softening point to be able to have flow and viscosity. To use Blown Asphalt 90/10 90/10, surfaces must be dry, clean, and free of loose particles, formwork, curing products, irregularities, slurry, etc.

Storage/handling of Blown Asphalt 90/10

Bitumen 90/10 has 10 years of validity with multi-time heating and cooling, please refer to MSDS.

Packing of Blown Asphalt 90/10

Various pickings are available for customer’s purpose and conveniences. bitumen 90/10 in various packing including Kraft bag, meltable plastic bag, drum, and bulk Blown Asphalt 90/10 90/10 from penetration grade bitumen, which is blown by hot air in a controlled process until the desired specification is reached. Blown Asphalt 90/10 can be supplied in any grade and are designated by two numbers to indicate the softening point and penetration ranges. The bitumen grade 90/10 means the softening point is 90°c and penetration is 10 desi millimeter is produced in compliance and conformity with ASTM standard and meets the following specification.

Specification of Oxidized Bitumen 90/10

Analysis of bitumen 90/10

Bitumen 90/10	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	5/15
Softening point °c	ASTM  D36	°C	85/95
Ductility @25 °c	ASTM  D113	Cm	1.5min
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Oxidized Bitumen 90/15

Oxidized Bitumen 90/15

At the Oxidized bitumen 90/15 production reactor, during the air acting, the mixture of the two Vacuum Bottom (VB) and Vacuum Silas (VS) feedstock is put under a special degree of pressure and temperature between 200-300˚C of which the hydrogen atoms content in bitumen molecular oxidize to the oxygen of the air, and obtains with higher hydrocarbons polymerization reaction that has lower penetration and higher softening points than the primary pure bitumen. This kind of bitumen 90/15 has the softening point of 90 and permeability of 15.
Oxidized bitumen is a specially formulated plastic for construction. Oxidized bitumen characterized by being a product of great thermal amplitude. Oxidized bitumen has the flexibility to cold, has no sag at high temperatures, and has good adhesion. It can be applied to any kind of work. Oxidized bitumen is available in different grades. Bitumen 90/15 is produced by either Continuous or Staggered Blowing Process. Heated Penetration Grade Bitumen under controlled environment is blown with air which controls the Oil Content in the Bitumen while it oxidized. The different grades for suited applications produced are designated by two numbers to indicate the mid-points of their softening point and penetration ranges.

As said before, Bitumen 90/15 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. In addition, the numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value measured by the Ring and Ball method as determined by ASTM D36. Also, the penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 90/15 Applications

Oxidized bitumen 90/15 uses in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, crack seal and repairmen, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The Oxidized asphalt 90/15 products are for paving. also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, a base for synthetic turf; typical uses for oxidized bitumen 90/15 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. Oxidized bitumen 90/15 is using the insulation and isolation bitumen membrane sheet. Also, Car undercoating Automobile industry is especially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof, and noise proof for automobile undercoating.

Oxidized bitumen 90/15 should be heated double temperature against the softening point to be able to have flow and viscosity. To use oxidized bitumen 90/15, surfaces must be dry, clean, and free of loose particles, formwork, curing products, irregularities, slurry, etc.

• Oxidized bitumen is used as a sealing of expansion joints.
• Oxidized bitumen is used as a repair of joints or cracks.
• Oxidized bitumen is used as a fixation of parquet floors.
• Oxidized bitumen is used as an adhesive to be used in thermal insulation.
• Oxidized bitumen is used as a repair of unexposed cracks.
• Oxidized bitumen is used as bonding of wet briquettes
• Oxidized bitumen is used in various industries like roofing, isolation, insulation flooring, mastics, pipe coatings, electrical applications.

Technical Advantages of Oxidized Asphalt 90/15

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Compared to paving grade bitumen:

• Reduced temperature susceptibility
• Exhibits a more ‘solid’ nature at ambient temperatures
• High penetration index

Recommendations for Handling / Storage

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

A note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Oxidized Asphalt material should be broken up prior to placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen, and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Oxidized Asphalt 90/15 to avoid overheating.

Packing of Oxidized Asphalt 90/15

Oxidized Asphalt 90/15 in various packing, including bitumen 90/15 is available in 20 & 50 kg Kraft Paper Bags / Poly Amide Bags, 25 kg Carton box, and 150, 180, 200kg Steel Drums. In addition, oxidized bitumen packing also palletize, 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Oxidized Asphalt 90/15 Specifications

Bitumen 90/15	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	10/20
Softening point °c	ASTM  D36	°C	85/95
Ductility @25 °c	ASTM  D113	Cm	1.5min
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Oxidized Bitumen 105/35

Oxidized Bitumen 105/35 Description

Oxidized bitumen 105/35 is a good grade of oxidized asphalt to use as bonding compounds as hot melt adhesive at an application rate of approximately 1 Kg/m3 to bond the preformed sheets together and to structure which is made by Oxidized bitumen 60/70 by hot air. Blown bitumen 105/35 is a semi-solid oxidized grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business.

Oxidized Bitumen 105/35 Applications

Oxidized bitumen 105/35 uses in the chemical, fuel, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, paint, crack seal and repairmen, civil works, roofing, construction business; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The bitumen 105/35 products are for paving. also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, the base for synthetic turf; typical uses for bitumen 105/35 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing. Blown bitumen 105/35 is using the insulation and isolation bitumen membrane sheet. The car undercoating Automobile industry is especially required for blown bitumen. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof, and noise proof for automobile undercoating.
Blown Asphalt 105/35 should be heated double temperature against the softening point to be able to have flow and viscosity. To use blown bitumen 105/35, surfaces must be dry, clean, and free of loose particles, formwork, curing products, irregularities, slurry, etc.

Storage/handling of blown bitumen 105/35

bitumen 105/35 has 10 years validity with multi-time heating and cooling, please refer to MSDS.

Packing of blown bitumen 105/35

Different packing is available for the customer’s purpose and convenience. bitumen 105/35 in different packing including Kraft bag, meltable plastic bag, drum, and bulk. Blown asphalt 105/35 from penetration grade bitumen, which is blown by hot air in a controlled process until the desired specification is reached. bitumen 105/35 can be supplied in any grade and are designated by two numbers to show the softening point and penetration ranges. The bitumen grade 105/35 means the softening point is 105 and penetration is 35 desi millimeters is produced in compliance and conformity with ASTM standard and meets the following specification.

Specification of blown bitumen 105/35

Analysis bitumen 105/35

Bitumen 105/35	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	30/40
Softening point °c	ASTM  D36	°C	100/110
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.

Oxidized Bitumen 105/15

Oxidized Bitumen 105/15 Description

Oxidized asphalt 105/15 (another word, blown asphalt 105/15, oxidized bitumen 105/15) is Semi Solid grade of pure petroleum bitumen manufactured by air-blowing through an asphalt flux. Special physical properties of its grade can be used in different applications in the construction business. Oxidized asphalt 105/15 is based on petroleum bitumen which is made by blowing bitumen 60/70 by very hot air. The numbers relate to the midpoint of the material’s softening point and penetration respectively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.

Oxidized Bitumen 105/15 Applications

Oxidized asphalt 105/15 uses in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, crack seal and repairmen, civil works, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The oxidized asphalt 105/15 products are for paving. also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, a base for synthetic turf; typical uses for asphalt 105/15 used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. Asphalt 105/15 is using the insulation and isolation bitumen membrane sheet. The car undercoating Automobile industry is especially required for Blown Asphalt. Vehicle undercoating material is based on Bitumen. Bitumen provides excellent waterproof, dustproof, and noise proof for automobile undercoating. The oxidized asphalt 105/15 should be heated double temperature against the softening point to support have flow and viscosity. To use asphalt 105/15, surfaces must be dry, clean and after loose particles, formwork, curing products, irregularities, slurry, etc.

Technical Advantages of Blown Bitumen 105/15

• Durability
• Flexibility
• Water-Resistant
• Chemical Stability

Storage and Handling

The heating of packaged bitumen is a critical phase in most of the final uses. Typically, the packaged material is heated and melted in boilers out on site.

However, control at the heating phase is very important in terms of health and safety as well as in maintaining the quality of the product.

The note must be taken of the maximum safe handling temperature of 230 C and this should not be abused. Bitumen is a poor conductor of heat, consequently, control of the heating phase is of paramount importance.

The Blown Bitumen material should be broken up before placement in the boiler. This exposes a larger surface area to the heat and encourages a more even heating regime. Without the larger exposed surface area, aggressive heating at the base and sides of the boiler may well result in localized overheating, altering the characteristics of the modified bitumen and potentially causing thermal cracking of the bitumen, creating the release of low lash vapors. The flashpoint of the oxidized bitumen then becomes irrelevant; as these low flash vapors determine the fire risk.

Melted bitumen should not be left in the boiler and reheated from cold, as there is then a high potential for localized overheating around the heating area (lack of convection means poor heat transfer) and potential development of a pressurized pocket of low flash vapors.

Be aware of the placement of any temperature monitoring or control devices. As a result of the poor thermal conductivity of the bitumen, a thermometer in the bitumen some distance from the heat source could read significantly different (even hundreds of degrees) from the true temperature of the bitumen near the heat source.

For Health and Safety information, please make reference to the relevant MSDS.

Health & Safety

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating Blown Bitumen 105/15 to avoid overheating.

Blown Asphalt 105/15 CHARACTERISTICS

CHARACTERISTIC	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM D5	mm/10	10/20
Softening point °c	ASTM D36	°C	100/110
Loss on heating(wt) %	ASTM D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Blown asphalt 105/15 Packing

Various packings are available for customer’s purpose and conveniences. TAVOIL CO is the manufacturer of asphalt 105/15 in various packing including Kraft bag, meltable plastic bag, drum, and bulk oxidized asphalt 105/15 from penetration grade bitumen.

TAVOIL asphalt 105/15 perchance is supplied in any grade and is designated by two numbers to indicate the softening point and penetration ranges. The oxidized asphalt grade 105/15 means the softening point is 105 and penetration are 15 desi millimeters is produced in compliance and conformity with ASTM standard and meets the following specification.

Oxidized Bitumen 150/5

Oxidized Bitumen 150/5 Description

Oxidized bitumen 150/5 is based on petroleum bitumen which is made by blowing bitumen 60/70 by hot air. This type of bitumen is hard and breakable. Oxidized bitumen 150/5 is the semi-solid oxidized grade of petroleum bitumen categorized in polycyclic aromatic hydrocarbons is normally used for different purposes in the construction industries. bitumen 150/5 should be heated double temperature (200ᵒ-300ᵒC) against the softening point to be able to have flow and viscosity. Normally heating of such hard oxidized bitumen should be arranged via hot oil by circulation inside of the isolated jacket. Bitumen oxide 150/5 from penetration grade bitumen, which is blown by hot air in a controlled process until the desired specification is reached. HJ Oil oxidized bitumen 150/5 can be supplied in any grade and are designated by two numbers to indicate the softening point and penetration ranges. The oxidized bitumen 150/5 means the softening point is 150°c and penetration is 15 desi millimeter is produced in compliance and conformity with ASTM standard.

Oxidized Bitumen 150/5 Applications

This Grade of Oxidized uses in the chemical, raw material for bitumen coat, lacquers, varnishes, paper-pulp-board, textile processing, pavement, crack seal and repairmen, civil works, bitumen coat for piping, roofing, construction industries; sealing and insulating buildings, adhesive, construction materials additive, road construction, dust-binding, insulating and impregnating agent, isolation bitumen membrane sheet, make rubber and plastic products. bitumen 150/5 products are for paving, roofing; also used in asphalt-based paints for corrosion protection of metals, inlining public works structures, adhesives in electrical laminates, the base for synthetic turf; typical uses for bitumen 150/5 include roofing, pipe coating, hydraulic applications, 150/5 is mainly using in paint manufacturing and coating in the hot area.

Before using bitumen 150/5 surfaces must be dry, clean, and free of loose particles, curing products, irregularities, and slurry. If you use this type of bitumen without cleaning the area the bitumen 150/5 will easily remove.

Blown Asphalt 150/5 Storage/handling

blown asphalt 150/5 has 10 years validity with multi-time heating and cold, please refer to MSDS. It is better to keep the bitumen 150/5 under shelter and out of the rain, the sun.

Blown Asphalt 150/5 Packing

bitumen 150/5 is available in 25 kg meltable and craft bag, drum, and bulk. Normally oxidized bitumen packing on the pallet and 40 bags can stack on the pallet. 20 pallets can load to the 20ft container.

Specification of Oxidized Bitumen 150/5

Analysis of Blown Asphalt 150/5

Bitumen 150/5	Test method	Unit	Specification
Specific gravity @25/25 C	ASTM D70	(Kg/m3)	1.05 approx.
Penetration @ 25°c	ASTM  D5	mm/10	4/6
Softening point °c	ASTM  D36	°C	145/155
Ductility @25 °c	ASTM  D113	Cm	1.5min
Loss on heating(wt) %	ASTM  D6	Wt. %	0.2 max
Flashpoint c	ASTM D92	°C	250 min
Solubility is CS2(wt) %	ASTM  D4	Wt. %	99.5 max
Spot test	A.A.S.H.O.T102	—	Negative

Health & Safety of Blown Asphalt 150/5

Workers should wear protective masks, gloves, and goggles during application. The asphalt can be removed from equipment and tools with kerosene or gasoline. Care should be taken when heating oxidized Bitumen 150/5 to avoid overheating.